HUIERJIE ZRO2 16.7% Premix is a high integrity chopped fibre, designed for using in dry mix systems or other premixing processes for subsequent molding into a GRC intricate component.
HUIERJIE ZRO216.7% High integrity has a low-tex strand which permits efficient reinforcement at low dosages. The coating size systems give easy incorporation whilst retaining best strand integrity, especially used in the electric closet panels.
HUIERJIE ZRO2 16.7% water dispersed can be simply added to the mix at the workshop without the need of a special equipment and disperse into filaments in a matrix of calcium silicate slurry, cement slurry etc.
Application:
The 'Premix' production technique involves pouring or pumping a cement/fibre mix into a mould, similar to other precast production processes. The mix is compacted using vibration or by adding other components. The unit is left in mould to set and demoulded the following day.Pre-mix has the advantages that moulds can be simper to produce and strip
| PREMIX CODE |
HIGH INTERGRITY CODE |
WATER DISPERSED |
ARC13-76-12MMH
ARC15-98-12MMH |
ARC11-40-12MMH |
ARC13-76-12MMHD
ARC15-98-12MMHD |
Technical DataType of glass Alkali Resistant (AR) Zirconia (ZrO2) content ≥16.7%Filament diameter um 13+2 11+2 15+2Strand tex 76+8 40+5 98+10Elastic modulus 80.4 Gpa Tensile strength 1.7 Gpa Length avaiable(MM) 6/12/18/20/24/30/36Moisture Content ≤0.2%Sizing Content 0.8 - 2.0% Breaking strength ≥0.32 N/tex
BENEFITS
Excellent alkali resistant and durability
Highest integrity during mix
Good fluidity
Been approved by Sheffied University,UK
Packaging&Storage
20kgs /kraft bag, 40bags/800Kg/pallet/109*109*105cm; 50bags /109*109*125cm,20palltes/ 1*20' FCL, N.W.18ton.
Huierjie AR Glassfibre roving pallet shall be stored dry in original packaging and advisable to stack in one layer, at a temperature between 15ºC- 35ºC & relative humidity between 35%- 65%.If stored below 15ºC, it is advisable to hold in workshop for 24 hours to prevent condensation before use.
Note:
Huierjie ARG Fiber are manufactured with high Zirconia rate in compliance with the BSEN 15422:2008 and ASTM C1666/C 1666/M-07 and under the recommendations of GRCA