Construction Material AR/ARG Glass Fibre Mesh
Application:
HUIERJIE AR GLASSFIBRE MAT is available in a range of nominal weight: standard is 150g/M2. It is produced by chopping Huierjie AR-Roving into 20-50mm strands and forming into a mat with a suitable binder. The mat has an open construction to permit penetration by cement mortar. The engineered binder, which dissolves with water further, assists incorporation into a cement matrix.
(1) It is used for layout, coating or mechanical formed GRC.
(2) It is used in roof waterproof and gypsum\marble\mosaic or board reinforcement.
(3)Reinforced material of internal and external insulation system of wall. Especially for External Thermal Insulation Composite Systems (ETICS). It can reinforce wall and prevent cracks. It is an ideal engineering material in construction.
HUIERJIE AR GLASSFIBRE MAT may be used as a positioned reinforcement flooring systems
AR MAT FOR GRC |
AR MESH FOR GRC |
ARMC150-1000L(H) ARMC225-1000L(H) ARMC300-1000L(H) |
ARNP10*10-100L(H)-160G/M2 ARNP5*5-100L(H)-160G/M2 ARNP6*6-100L(H)- 270G/M2 |
MAT Technical Data
- EXAMPLE ARMC150-1000H
- Type of glass Alkali Resistant (AR)
- Zirconia (ZrO2) content ≥16.7%
- Filament diameter (μm) 11+2
- Strand tex 50+5
- Weight available(g/m2) 150 225 300
- WIDTH(MM) 1000
- Sizing Content 9%
- Breaking strength(N/150MM) 37
MESH Technical Data
- EXAMPLE ARNP5*5-100-160G/M2
- ]Type of glass Alkali Resistant (AR)
- Zirconia (ZrO2) content ≥16.7%
- Hole Distance(mm) 5
- Weight available(g/m2) 145 160 270
- WIDTH(MM) 1000
- WARP DIRECTION TENSILE STRENGTH (N/50mm) 1356
- WEFT DIRECTION TENSILE STRENGTH (N/50mm) 1290
- LATEX COATING Content 20%
- Strength Remained rate after soaked in
cement filtrate for 28 days ≥90%
MAT Packing details: 100M2 /Roll /ctn,16ctns/pallet,20pallets/1*20'FCL. 32000m2.
MESH Packing details: 50M2/Roll, 36rolls/pallet, 20pallets/1*20'FCL. 36000m2.
Properties:
Good stableness, Good cohesion with concret, High strength, elastic modulus up to 80.4Gpa, High alkali resistant, Strain breaking point: 2.4%
Storage
Huierjie AR Glassfibre mat & mesh pallet shall be stored dry in original packaging and advisable to stack in one layer, at a temperature between 15ºC- 35ºC & relative humidity between 35%- 65%.If stored below 15ºC, it is advisable to hold in workshop for 24 hours to prevent condensation before use.
Note:
Huierjie AR Glassfibre mesh are manufactured in compliance with EN15422:2008, BSEN13496:2002 and ETAG 004.
HUIERJIE AR GLASSFIBRE MESH is used by Manual laying or Mechanical molding to reinforce the areas which need mechanical strength to prevent crack.